Study on the Analysis of Damage Patterns of Cellular Phone Batteries According to Energy Sources
Chung-Seog Choi · 2011
The purpose of this paper is to present the damage patterns of cellular phone (SCH_W830) batteries according to energy sources and have them utilized as data for the settlement of disputes between manufactures and consumers. The reliability was secured by maintaining the ambient temperature and humidity at and 40~60 %, respectively. The voltage of the battery used for the tests was measured to be 4.18V between positive pole (+) and negative pole (-)(1), and 4.19 V between positive pole (+) and negative pole (-)(2). This study applied the Korean Industrial Standard (KS) to the flammability test of cellular phones due to a general flame applied to them and found that no damage occurred to the built-in battery even though the flame was applied to the cases of cellular phones for 30 seconds. From the results of immersing the cellular phones in the saline solution (NaCl, 0.9 %) for 180 seconds, it was found that there was a trace of carbonization and melting due to the heat caused by leaking current. It can be seen that when the cellular phones were heated for 70 seconds using a microwave oven (MWO), the areas containing the metal holder, recharging connector, antenna, etc., were melted and discolored and that other areas showed no particular problems. That is, while the external carbonization of cellular phones, built-in metals and dielectric materials, and damage and deformation of the battery terminal block, etc., occurred differently depending on the types of energy sources, the voltage showed comparatively constant characteristics. Therefore, it is thought to be possible to attribute the cause of damage to the battery by performing analysis taking into consideration comprehensively the characteristics of the flame spread pattern as well as the melting and deformation of metals.